普通混凝土结构中的钢筋锈蚀及防腐蚀措施
摘要:钢筋锈蚀是最常见的混凝土结构破坏现象之一,特别是在复杂的恶劣环境工作下的混凝土结构,钢筋锈蚀更为普遍存在。因此,对于混凝土结构中钢筋的防腐蚀措施在设计和施工阶段变得尤为的重要。本文主要介绍了混凝土结构中钢筋锈蚀机理及影响钢筋锈蚀的多种因素,同时还提出一些关于混凝土结构设计和施工中可以采取的防腐蚀措施。
关键词:钢筋锈蚀;混凝土结构;防腐蚀;结构破坏
Abstract:Corrosion of reinforcement is one of the most common phenomenon of concrete structural damage, especially among the concrete structure that works in the complex environments, corrosion of reinforcement is more common. Therefore, the anti-corrosion measures for reinforcement in design and construction is particularly important in concrete structures. This article mainly introduced the corrosion mechanism of reinforcement in concrete structures and the various of the influence factors, meanwhile it also put forward some anti-corrosion measures in the concrete structure design and construction.
Key words:corrosion of reinforcement ;concrete structure ;anti-corrosion;
structural damage
近年来,混凝土在房屋建筑、公路、桥梁、大坝等结构中得到广泛的应用。同时,此结构在长期自然环境和使用条件下会出现逐渐老化、损伤甚至破坏,从而有可能会直接影响到结构的安全,因此混凝土耐久性成为社会关注的问题之一,也曾给世界各国带来巨大的经济损失[6]。混凝土耐久性是指混凝土结构在自然环境、使用环境及材料内部因素作用下保持其工作能力的性能。当混凝土中水泥发生水化作用之后会在钢筋表面形成一层保护膜,但是此保护膜破坏后,在足够的条件下,混凝土中的钢筋就会发生腐蚀,从而导致钢筋截面减小,钢筋表面与混凝土的粘结力下降,最终导致结构破坏。
混凝土结构中的钢筋锈蚀可分为自然电化学腐蚀和杂散电流腐蚀。而对于一般的混凝土结构中发生的钢筋锈蚀通常是自然电化学腐蚀[1],如钢筋碳化锈蚀和氯盐锈蚀。
1 混凝土中钢筋锈蚀机理及影响因素
1.1混凝土中钢筋锈蚀机理
钢筋表面钝化膜要在较高的碱性环境下(pH≥10) 才能存在,而当碳化后的碱性降到pH = 9 甚至以下此钝化膜就变得很不稳定[4],就会遭到破坏,破坏后在
普通混凝土结构中的钢筋锈蚀及防腐蚀措施
摘要:钢筋锈蚀是最常见的混凝土结构破坏现象之一,特别是在复杂的恶劣环境工作下的混凝土结构,钢筋锈蚀更为普遍存在。因此,对于混凝土结构中钢筋的防腐蚀措施在设计和施工阶段变得尤为的重要。本文主要介绍了混凝土结构中钢筋锈蚀机理及影响钢筋锈蚀的多种因素,同时还提出一些关于混凝土结构设计和施工中可以采取的防腐蚀措施。
关键词:钢筋锈蚀;混凝土结构;防腐蚀;结构破坏
Abstract:Corrosion of reinforcement is one of the most common phenomenon of concrete structural damage, especially among the concrete structure that works in the complex environments, corrosion of reinforcement is more common. Therefore, the anti-corrosion measures for reinforcement in design and construction is particularly important in concrete structures. This article mainly introduced the corrosion mechanism of reinforcement in concrete structures and the various of the influence factors, meanwhile it also put forward some anti-corrosion measures in the concrete structure design and construction.
Key words:corrosion of reinforcement ;concrete structure ;anti-corrosion;
structural damage
近年来,混凝土在房屋建筑、公路、桥梁、大坝等结构中得到广泛的应用。同时,此结构在长期自然环境和使用条件下会出现逐渐老化、损伤甚至破坏,从而有可能会直接影响到结构的安全,因此混凝土耐久性成为社会关注的问题之一,也曾给世界各国带来巨大的经济损失[6]。混凝土耐久性是指混凝土结构在自然环境、使用环境及材料内部因素作用下保持其工作能力的性能。当混凝土中水泥发生水化作用之后会在钢筋表面形成一层保护膜,但是此保护膜破坏后,在足够的条件下,混凝土中的钢筋就会发生腐蚀,从而导致钢筋截面减小,钢筋表面与混凝土的粘结力下降,最终导致结构破坏。
混凝土结构中的钢筋锈蚀可分为自然电化学腐蚀和杂散电流腐蚀。而对于一般的混凝土结构中发生的钢筋锈蚀通常是自然电化学腐蚀[1],如钢筋碳化锈蚀和氯盐锈蚀。
1 混凝土中钢筋锈蚀机理及影响因素
1.1混凝土中钢筋锈蚀机理
钢筋表面钝化膜要在较高的碱性环境下(pH≥10) 才能存在,而当碳化后的碱性降到pH = 9 甚至以下此钝化膜就变得很不稳定[4],就会遭到破坏,破坏后在