大型耳轴锻件热处理工艺研究
作者:郎庆斌 郑三妹 殷立涛 于慎君 李光 刘晓恩
来源:《上海有色金属》2013年第04期
收稿日期: 2013-04-06
作者简介: 郎庆斌(1980-),男,硕士,工程师. 主要从事大型铸锻件的材料及热处理技术研究、齿轮渗碳工艺技术研究.
E-mail: [email protected].
摘 要: 通过对18CrMnMoB 钢进行不同温度的淬火、回火调质处理,测定其力学性能,并对其显微组织进行对比分析,找出合理的热处理工艺范围. 结果表明:18CrMnMoB 钢的最佳淬火温度范围为880~900 ℃,大型耳轴水淬后在560~580 ℃回火,具有良好的强韧性,性能完全达到技术要求.
关键词: 18CrMnMoB钢; 力学性能; 淬火温度; 耳轴
中图分类号: TG 156.6 文献标志码: A
Study on Heat Treatment Process of Large Trunnion Forging
LANG Qing-bin, ZHENG San-mei, YIN Li-tao,
YU Shen-jun, LI Guang, LIU Xiao-en
(CITIC Heavy Industries Co. , Ltd. , Luoyang 200093, China)
Abstract: Testing research on metallurgical and property of 18CrMnMoB steel was made at different temperature to process quenching-tempering in order to determine the best temperature for the process. The results showed that the best quenching-temperature is 880~900 ℃. For large trunnion forging, best result with very strong toughness can be achieved to meet the technical requirements after it being processed under water quenching and then tempered at 560~580 ℃. Key words: 18CrMnMoB steel; mechanical property; quenching temperature; large trunnion forging
0 前 言
炼钢转炉上的耳轴是转炉倾动装置的重要组成部分,其工作条件高温、多尘,会使耳轴产生挠曲变形,因此,要求耳轴具有足够的强度和韧性[1].18CrMnMoB钢具有良好的淬透性、锻
龙源期刊网 http://www.qikan.com.cn
大型耳轴锻件热处理工艺研究
作者:郎庆斌 郑三妹 殷立涛 于慎君 李光 刘晓恩
来源:《上海有色金属》2013年第04期
收稿日期: 2013-04-06
作者简介: 郎庆斌(1980-),男,硕士,工程师. 主要从事大型铸锻件的材料及热处理技术研究、齿轮渗碳工艺技术研究.
E-mail: [email protected].
摘 要: 通过对18CrMnMoB 钢进行不同温度的淬火、回火调质处理,测定其力学性能,并对其显微组织进行对比分析,找出合理的热处理工艺范围. 结果表明:18CrMnMoB 钢的最佳淬火温度范围为880~900 ℃,大型耳轴水淬后在560~580 ℃回火,具有良好的强韧性,性能完全达到技术要求.
关键词: 18CrMnMoB钢; 力学性能; 淬火温度; 耳轴
中图分类号: TG 156.6 文献标志码: A
Study on Heat Treatment Process of Large Trunnion Forging
LANG Qing-bin, ZHENG San-mei, YIN Li-tao,
YU Shen-jun, LI Guang, LIU Xiao-en
(CITIC Heavy Industries Co. , Ltd. , Luoyang 200093, China)
Abstract: Testing research on metallurgical and property of 18CrMnMoB steel was made at different temperature to process quenching-tempering in order to determine the best temperature for the process. The results showed that the best quenching-temperature is 880~900 ℃. For large trunnion forging, best result with very strong toughness can be achieved to meet the technical requirements after it being processed under water quenching and then tempered at 560~580 ℃. Key words: 18CrMnMoB steel; mechanical property; quenching temperature; large trunnion forging
0 前 言
炼钢转炉上的耳轴是转炉倾动装置的重要组成部分,其工作条件高温、多尘,会使耳轴产生挠曲变形,因此,要求耳轴具有足够的强度和韧性[1].18CrMnMoB钢具有良好的淬透性、锻