宝钢搪瓷用钢的开发与应用
孙全社
(宝钢股份公司技术中心, 上海201900)
【摘要】 , 阐述搪瓷钢板在成形性能、抗鳞爆性能以及强度等方面的要求, 结果表明, 宝钢
【关键词】 搪瓷钢板 OF ENAME LING SHEET
STEE LS AT BAOSTEE L
Sun Quanshe
(Baoshan Iron and Steel C o. , Ltd. )
【Abstract 】 The chemical com positions and processing procedure of the cold 2rolled ultra low
carbon sheet steels and hot 2rolled sheet steels for enameling use were briefly introduced , and the properties of formability , fish scale resistance and strength were dem onstrated. The exam ples were given to show that the hot and cold rolled steel sheets were applied to manu facture bath tub , BBQ , decoration panel and inter flask of the thermal heater , and etc. The application results showed that the various types of enameling steels could meet the production needs of the various enameling ware.
【K ey Words 】 Enameling Steel Sheet , Chemical C om position , Production Process , Property ,
Development and Application 1 前 言
搪瓷钢板在国民经济中发挥着十分重要的作用, 在日常生活中与人们的关系十分密切, 广泛地应用于轻工、家电、冶金、化工、建筑等行业, 制作厨房用具、卫生洁具、烧烤炉、热水器内胆、建筑饰面板、化工反应罐等等。搪瓷钢板的种类很多, 按生产工艺分有热轧板(酸洗板) 、冷轧板和覆层板等; 按搪瓷工艺分有一次搪瓷和两次搪瓷, 单面搪瓷和双面搪瓷, 湿法搪瓷和静电干粉搪瓷等; 按成形性能可分为C Q 、DQ 、DDQ 到E DDQ 等不同冲压级别; 从强度上可分为如245MPa 、330MPa 等不同的强度级别。
搪瓷钢板的性能要求主要包括强度、成形性、抗鳞爆性、密着性和焊接性等方面, 不同用途的搪瓷钢板, 要求具备不同的综合性能。
近几年, 宝钢开发了冷轧超深冲搪瓷钢板(BT C1) 、热轧深冲搪瓷钢板和热轧高强度搪瓷钢板系列, 供国内外用户使用, 受到普遍欢迎。2 宝钢搪瓷钢板的品种及其生产工艺宝钢自1997年以来针对市场的需求开发出新一代的搪瓷专用钢。搪瓷钢板的种类、特点和用途见表1。211 冷轧超深冲搪瓷钢板
冷轧超深冲搪瓷钢是一种以超低碳钢为基础、通过添加适量的合金元素并严格控制生产工艺, 达到既具有高延伸率、高n 值和r 值、无时效性, 又具有优良的涂搪性能的搪瓷专用钢。这是为了适应人们对搪瓷制品的形状和质量要求日益提高的需要而开发的, 特别适合于冲制形状复杂、冲压难度大、搪瓷质量要求高的搪瓷制品如裙边浴缸等。
作者简介:孙全社(1965-) , 男, 高级工程师, Email :sunqs @Baosteel 1com
48
上 海 金 属
第27卷
国外最初以脱碳退火方式降低钢的碳含量。随着冶金水平的提高和工艺技术的进步, 尤其是真空脱气、炉外精炼、连铸技术、控轧控冷和连续退火的应用与发展, 使得超低碳钢的冶金生产成为可能, 因此大大地提高了钢板的质量及其稳定性, 促进了超低碳搪瓷钢的发展。
宝钢冷轧超深冲搪瓷钢的生产工艺如下:转炉冶炼→真空脱气→连铸→热轧→酸洗→冷轧→退火→平整、剪切、涂油和包装。212 对热轧高强度搪瓷钢板来说, 宝钢按钢板的
屈服强度分为245MPa 、330MPa 等级别, 主要用于生产热水器内胆、化工反应罐等耐压容器。钢板的强度级别不同, 对应的成形性要求也不同。
宝钢高强度热轧搪瓷板以酸洗板表面状态交货, 生产工艺流程为:→真空脱气→连铸→→、涂油和包装。1, 主要用于生产成形较复杂、搪瓷质量要求高的制品如烧烤炉等, 可以部分替代冷轧板, 因而其应用范围较广。其生产工艺流程同热轧高强度搪瓷钢。3 宝钢搪瓷钢的成分要求和性能特点311 化学成分
由于冶金装备的发展和技术水平的提高, 特别是超低碳、超低氮和超低硫钢的冶炼水平的提高和连铸工艺的采用, 使得纯净钢的生产得到了快速的发展。但是, 纯净钢由于钢质纯净, 使得贮氢的氢陷阱减少, 导致钢板的抗鳞爆性能变差, 因而无法满足搪瓷的要求。为此需在钢中添加合金元素以在钢中形成一定的夹杂物和析出物, 并控制尺寸和分布, 使钢板既具有优良的成形性能又具有优良的抗鳞爆性能。
宝钢搪瓷钢板的化学成分要求见表2。
表2 宝钢搪瓷钢的化学成分要求(%)
牌号
BT C1
C
S i
Mn
P
S
Al
级别和冲压性能, 性能。其性能特点和用途见表1。
在搪瓷制品的生产过程中, 除了要求钢板具有良好的涂搪性能外, 针对不同用途, 要求具有不同的强度级别, 如生产耐压的热水器内胆等既要求钢板具有良好的成形性, 满足内胆封头的冲压成形, 又要有较高的强度, 保证内胆能够承受压强为110～112MPa 的耐压试验和高压水循环试验, 以及良好的焊接性, 使焊缝处及热影响区在涂搪性能和耐压能力方面不致于成为薄弱环节。对于一些难冲件则需要有良好的深冲性以满足成形的要求, 所以只有不同强度级别和冲压级别的热轧钢板才能够满足各种搪瓷制品的不同需要。
表1 宝钢搪瓷钢板的种类、性能和用途
牌号
产品类型超低碳超
BTC1
性能特点超深冲性能优良的抗鳞爆性能优良的密着性能优良的抗挠性能深冲性能优良的抗鳞爆性能优良的密着性能较高强度良好的冲压性能良好的抗鳞爆性能优良的密着性能高强度较好的冲压性能良好的抗鳞爆性能良好的密着性能
用 途
其它合金元素
厨具、卫具、烧烤炉、建筑面板等浴缸、烧烤炉、烤箱等
深冲冷轧钢板超低碳深
Φ01008BT C330R Φ0116BT C245R Φ0116BT C3R Φ01008Φ01030110～0130
Φ0105Φ0190Φ0105Φ0190Φ0105Φ0150Φ01020
Φ0107Φ0107Φ01020Φ0105Φ0105Φ0105Φ0105Φ0107T i 等Ε0102有Ε0102有Φ0107有
BTCR3冲热轧酸洗钢板高强度热
BTC245R 轧酸洗钢
热水器内胆等
板
高强度热
BTC330R 轧酸洗钢
从表可见, 宝钢的超深冲搪瓷钢板(BT C1) 以超低碳钢为基础, 通过加入适量的合金元素, 实现超深冲性能和优良的抗鳞爆性能。高强度搪瓷钢则基于低碳钢, 并适当地加入合金元素, 实现强度、塑性和涂搪性的良好匹配。312 性能要求
热水器内胆、化工罐等
板
宝钢搪瓷钢的力学性能要求见表3。
第6期
孙全社:宝钢搪瓷用钢的开发与应用
表3 宝钢搪瓷钢的力学性能要求
31213 抗挠性能
r 值
49
牌号
BTC1BTC330R BTC245R BTCR
σMPa s ΠΦ190
Ε330Ε245Φ190
σMPa b Π
270～320
δ50Π%Ε43
Ε22Ε28Ε35
n 值
挠曲是钢板经搪烧以后发生变形的原因之一。钢板的抗挠性与板厚、晶粒度和化学成分有关
[6]
Ε0119
---
Ε116
---
Ε400Ε340Ε275
。
比较超低碳含钛搪瓷钢与脱碳压盖钢的挠度
[7]
表明
搪瓷钢板的成形性能、强度和涂搪性能等性能要求与其加工工艺密切相关。。31211 成形性能
, 。BT C1由于T i 合金, 因此其耐, 特别适合于制做表面质量和尺寸精度要求高的搪瓷面板等。31214 搪瓷密着性
、, 通过适量的合金配比、高温终轧和高温退火等工艺, 控制钛在钢中的析出行为, 促进铁素体晶粒的长大和{111}等再结晶织构的发展, 以实现高的延伸率、高n 值、高r 值和无时效性
[1]
瓷层与基板之间的结合力即搪瓷密着性。宝钢在搪瓷钢的生产过程中, 一方面依靠添加适当的合金元素, 有利于钢板与瓷釉结合, 另一方面在精整时采用特殊的轧辊进行平整, 控制钢板的表面结构, 实现良好的密着性能。31215 搪烧后的强度
。宝钢还开发了加稀土的超低碳钢, 该钢既
[2]
有超深冲性能又具优良的涂搪性能。热轧深冲
钢也基于超低碳钢, 通过控制热轧工艺来提高钢板的成形性。热轧高强钢系列则主要通过细化晶粒、析出强化和晶溶强化等强化机制提高钢板强度的同时, 保证钢板具有一定的成形性。31212 抗鳞爆性能
宝钢的高强度搪瓷钢板由于添加了合金元素钛, 提高了搪烧后钢板的强度稳定性。试验表明, 即使在高于通常的搪烧温度下也能保证钢板具有较高的强度。图1是宝钢BT C330R 经高温搪烧后的力学性能, 可以看出即使经高温长时间的模拟搪烧后钢板的强度下降仍然很小, 也即钢板具有良好的高温稳定性
。
抗鳞爆性能是搪瓷钢板应有的最基本、也是最重要的性能指标之一。导致搪瓷制品产生鳞爆是由氢造成的, 氢主要是在酸洗和搪烧过程中进入钢板的, 所以除了改进搪瓷工艺外, 还应改善钢板本身的抗鳞爆性能。如果氢在钢板中扩散得慢, 在相同的搪瓷工艺下进入钢板中的氢就少, 这将有利于防止搪瓷制品的鳞爆。
钢中的晶界、位错、空穴、夹杂物和析出相等都是良好的氢陷阱, 但超低碳钢由于钢质纯净没有足够的氢陷阱, 满足不了搪瓷时抗鳞爆的需要, 因此对于搪瓷钢, 需要针对不同的搪瓷用途, 调整钢的成分和生产工艺, 以保证钢中有足够的氢陷阱, 实现良好的抗鳞爆性能。
在宝钢生产的搪瓷钢板中, 由于添加了足够的T i 、RE 和B 等合金元素, 它们在钢中与C 、N 和S 元素化合, 形成了足够的第二相粒子, 这些第二相粒子尺寸细小呈弥散分布, 成为良好的贮氢陷阱, 从而提高了钢板的抗鳞爆性能
[3～5]
图1 不同搪烧温度下保温时间对钢板 力学性能的影响4 搪瓷钢的实物性能和应用
典型的宝钢生产的搪瓷钢的实物性能见表4。
。
50
上 海 金 属
表4 搪瓷钢板典型的力学性能
第27卷
牌号
BTC1BTC245R BTC330R
MPa σMPa 厚度Πmm σs Πb Π115210116
140270345
306386454
δ50Π%
504130
n m 0124--
r m 210--
宝钢冷轧搪瓷钢板BT C1和热轧高强度搪瓷钢板BT C330R 的部分应用实例分别见图2和图3。经过大批量的使用证明, 其综合性能完全满
足用户的要求。另外, BT C245R 和BT CR3也具备大批量的供货条件
。
注:表中n m 、r m 值分别为钢板沿与轧制方向呈0°、45°、
90°方向的n 值和r 值的平均值。
(a ) 裙边浴缸 (b ) 建筑饰面板 (c ) 烧烤炉
图2 宝钢BT C1
的应用举例
品, 也可用于替代部分冷轧搪瓷钢板。
宝钢正利用现有的工艺装备继续搪瓷钢板的开发, 以满足用户的不同需求, 为用户的发展提供更大的空间。
参考文献
[1]孙全社等1加钛超低碳钢的成形性能和贮氢性能的研究1
钢铁. 2000, 35(1) :39～42
[2]孙全社等. RE 、T i 和Nb 对冷轧超低碳搪瓷钢板成形性能的
图3 宝钢BT C330R 的应用举例
5 结 语
影响. 钢铁研究学报. (待发表)
[3]孙全社. 冷轧超低碳搪瓷钢板的试验研究. 宝钢技术.
2000, (3) :22～24, 58
[4]袁晓敏, 张庆安, 孙全社. 搪瓷钢板中析出物的测定. 钢
经过几年的开发和实践, 宝钢的搪瓷钢板已基本形成系列化, 能够满足不同用户的需求:
(1) 超深冲冷轧搪瓷钢板具有优良的成形性能(即高的延伸率、高n 值和高r 值) 、无时效性和优良的涂搪性能, 用于深冲浴缸、烧烤炉和建筑饰面板等。
(2) 高强度热轧钢系列不仅具有高强度、良好的成形性、焊接性和涂搪性, 而且经搪烧后具有较高的强度, 能够满足不同冲压难度的热水器内胆的生产要求。
(3) 热轧深冲用钢既具有深冲性能, 又能满足双面搪瓷的要求, 特别适合于生产烧烤炉等产
铁研究学报. 2000, 12(5) :58～60
[5]Sun Quanshe , Jing Lei , Lv Feng , et al. S tudy on Hydrogen
Permeability of T itanium -Bearing Ultra Low Carbon Sheet S teel. Prodeedings of the 4th International HS LA S teels ’2000(in X i ’an ) , edited by Liu G uoquan , W ang Fum ing , W ang Zubin , Zhang H ongtao , organized by the Chinese S ociety for M etals , 635～638[6]安田显ら. 连铸制深绞りほうろう用钢板の制造. 川崎制铁
技报. 1984, 16(4) :280～287; 1994, 34, (1) :17～23
[7]L. M eyer , W. Bleck , W. Muschenborn. Product -oriented IF
S teel Design. ISI J Int. , S pecial Issue on Physical M etallurgy of Ultralow Carbon Interstitial -free S teels. 1994, :203～222
收修改稿日期:2005204220
第27卷 第6期
2005年11月
上 海 金 属
SH ANG H AI MET A LS
V ol 127, N o 16 47N ovember , 2005
宝钢搪瓷用钢的开发与应用
孙全社
(宝钢股份公司技术中心, 上海201900)
【摘要】 , 阐述搪瓷钢板在成形性能、抗鳞爆性能以及强度等方面的要求, 结果表明, 宝钢
【关键词】 搪瓷钢板 OF ENAME LING SHEET
STEE LS AT BAOSTEE L
Sun Quanshe
(Baoshan Iron and Steel C o. , Ltd. )
【Abstract 】 The chemical com positions and processing procedure of the cold 2rolled ultra low
carbon sheet steels and hot 2rolled sheet steels for enameling use were briefly introduced , and the properties of formability , fish scale resistance and strength were dem onstrated. The exam ples were given to show that the hot and cold rolled steel sheets were applied to manu facture bath tub , BBQ , decoration panel and inter flask of the thermal heater , and etc. The application results showed that the various types of enameling steels could meet the production needs of the various enameling ware.
【K ey Words 】 Enameling Steel Sheet , Chemical C om position , Production Process , Property ,
Development and Application 1 前 言
搪瓷钢板在国民经济中发挥着十分重要的作用, 在日常生活中与人们的关系十分密切, 广泛地应用于轻工、家电、冶金、化工、建筑等行业, 制作厨房用具、卫生洁具、烧烤炉、热水器内胆、建筑饰面板、化工反应罐等等。搪瓷钢板的种类很多, 按生产工艺分有热轧板(酸洗板) 、冷轧板和覆层板等; 按搪瓷工艺分有一次搪瓷和两次搪瓷, 单面搪瓷和双面搪瓷, 湿法搪瓷和静电干粉搪瓷等; 按成形性能可分为C Q 、DQ 、DDQ 到E DDQ 等不同冲压级别; 从强度上可分为如245MPa 、330MPa 等不同的强度级别。
搪瓷钢板的性能要求主要包括强度、成形性、抗鳞爆性、密着性和焊接性等方面, 不同用途的搪瓷钢板, 要求具备不同的综合性能。
近几年, 宝钢开发了冷轧超深冲搪瓷钢板(BT C1) 、热轧深冲搪瓷钢板和热轧高强度搪瓷钢板系列, 供国内外用户使用, 受到普遍欢迎。2 宝钢搪瓷钢板的品种及其生产工艺宝钢自1997年以来针对市场的需求开发出新一代的搪瓷专用钢。搪瓷钢板的种类、特点和用途见表1。211 冷轧超深冲搪瓷钢板
冷轧超深冲搪瓷钢是一种以超低碳钢为基础、通过添加适量的合金元素并严格控制生产工艺, 达到既具有高延伸率、高n 值和r 值、无时效性, 又具有优良的涂搪性能的搪瓷专用钢。这是为了适应人们对搪瓷制品的形状和质量要求日益提高的需要而开发的, 特别适合于冲制形状复杂、冲压难度大、搪瓷质量要求高的搪瓷制品如裙边浴缸等。
作者简介:孙全社(1965-) , 男, 高级工程师, Email :sunqs @Baosteel 1com
48
上 海 金 属
第27卷
国外最初以脱碳退火方式降低钢的碳含量。随着冶金水平的提高和工艺技术的进步, 尤其是真空脱气、炉外精炼、连铸技术、控轧控冷和连续退火的应用与发展, 使得超低碳钢的冶金生产成为可能, 因此大大地提高了钢板的质量及其稳定性, 促进了超低碳搪瓷钢的发展。
宝钢冷轧超深冲搪瓷钢的生产工艺如下:转炉冶炼→真空脱气→连铸→热轧→酸洗→冷轧→退火→平整、剪切、涂油和包装。212 对热轧高强度搪瓷钢板来说, 宝钢按钢板的
屈服强度分为245MPa 、330MPa 等级别, 主要用于生产热水器内胆、化工反应罐等耐压容器。钢板的强度级别不同, 对应的成形性要求也不同。
宝钢高强度热轧搪瓷板以酸洗板表面状态交货, 生产工艺流程为:→真空脱气→连铸→→、涂油和包装。1, 主要用于生产成形较复杂、搪瓷质量要求高的制品如烧烤炉等, 可以部分替代冷轧板, 因而其应用范围较广。其生产工艺流程同热轧高强度搪瓷钢。3 宝钢搪瓷钢的成分要求和性能特点311 化学成分
由于冶金装备的发展和技术水平的提高, 特别是超低碳、超低氮和超低硫钢的冶炼水平的提高和连铸工艺的采用, 使得纯净钢的生产得到了快速的发展。但是, 纯净钢由于钢质纯净, 使得贮氢的氢陷阱减少, 导致钢板的抗鳞爆性能变差, 因而无法满足搪瓷的要求。为此需在钢中添加合金元素以在钢中形成一定的夹杂物和析出物, 并控制尺寸和分布, 使钢板既具有优良的成形性能又具有优良的抗鳞爆性能。
宝钢搪瓷钢板的化学成分要求见表2。
表2 宝钢搪瓷钢的化学成分要求(%)
牌号
BT C1
C
S i
Mn
P
S
Al
级别和冲压性能, 性能。其性能特点和用途见表1。
在搪瓷制品的生产过程中, 除了要求钢板具有良好的涂搪性能外, 针对不同用途, 要求具有不同的强度级别, 如生产耐压的热水器内胆等既要求钢板具有良好的成形性, 满足内胆封头的冲压成形, 又要有较高的强度, 保证内胆能够承受压强为110～112MPa 的耐压试验和高压水循环试验, 以及良好的焊接性, 使焊缝处及热影响区在涂搪性能和耐压能力方面不致于成为薄弱环节。对于一些难冲件则需要有良好的深冲性以满足成形的要求, 所以只有不同强度级别和冲压级别的热轧钢板才能够满足各种搪瓷制品的不同需要。
表1 宝钢搪瓷钢板的种类、性能和用途
牌号
产品类型超低碳超
BTC1
性能特点超深冲性能优良的抗鳞爆性能优良的密着性能优良的抗挠性能深冲性能优良的抗鳞爆性能优良的密着性能较高强度良好的冲压性能良好的抗鳞爆性能优良的密着性能高强度较好的冲压性能良好的抗鳞爆性能良好的密着性能
用 途
其它合金元素
厨具、卫具、烧烤炉、建筑面板等浴缸、烧烤炉、烤箱等
深冲冷轧钢板超低碳深
Φ01008BT C330R Φ0116BT C245R Φ0116BT C3R Φ01008Φ01030110～0130
Φ0105Φ0190Φ0105Φ0190Φ0105Φ0150Φ01020
Φ0107Φ0107Φ01020Φ0105Φ0105Φ0105Φ0105Φ0107T i 等Ε0102有Ε0102有Φ0107有
BTCR3冲热轧酸洗钢板高强度热
BTC245R 轧酸洗钢
热水器内胆等
板
高强度热
BTC330R 轧酸洗钢
从表可见, 宝钢的超深冲搪瓷钢板(BT C1) 以超低碳钢为基础, 通过加入适量的合金元素, 实现超深冲性能和优良的抗鳞爆性能。高强度搪瓷钢则基于低碳钢, 并适当地加入合金元素, 实现强度、塑性和涂搪性的良好匹配。312 性能要求
热水器内胆、化工罐等
板
宝钢搪瓷钢的力学性能要求见表3。
第6期
孙全社:宝钢搪瓷用钢的开发与应用
表3 宝钢搪瓷钢的力学性能要求
31213 抗挠性能
r 值
49
牌号
BTC1BTC330R BTC245R BTCR
σMPa s ΠΦ190
Ε330Ε245Φ190
σMPa b Π
270～320
δ50Π%Ε43
Ε22Ε28Ε35
n 值
挠曲是钢板经搪烧以后发生变形的原因之一。钢板的抗挠性与板厚、晶粒度和化学成分有关
[6]
Ε0119
---
Ε116
---
Ε400Ε340Ε275
。
比较超低碳含钛搪瓷钢与脱碳压盖钢的挠度
[7]
表明
搪瓷钢板的成形性能、强度和涂搪性能等性能要求与其加工工艺密切相关。。31211 成形性能
, 。BT C1由于T i 合金, 因此其耐, 特别适合于制做表面质量和尺寸精度要求高的搪瓷面板等。31214 搪瓷密着性
、, 通过适量的合金配比、高温终轧和高温退火等工艺, 控制钛在钢中的析出行为, 促进铁素体晶粒的长大和{111}等再结晶织构的发展, 以实现高的延伸率、高n 值、高r 值和无时效性
[1]
瓷层与基板之间的结合力即搪瓷密着性。宝钢在搪瓷钢的生产过程中, 一方面依靠添加适当的合金元素, 有利于钢板与瓷釉结合, 另一方面在精整时采用特殊的轧辊进行平整, 控制钢板的表面结构, 实现良好的密着性能。31215 搪烧后的强度
。宝钢还开发了加稀土的超低碳钢, 该钢既
[2]
有超深冲性能又具优良的涂搪性能。热轧深冲
钢也基于超低碳钢, 通过控制热轧工艺来提高钢板的成形性。热轧高强钢系列则主要通过细化晶粒、析出强化和晶溶强化等强化机制提高钢板强度的同时, 保证钢板具有一定的成形性。31212 抗鳞爆性能
宝钢的高强度搪瓷钢板由于添加了合金元素钛, 提高了搪烧后钢板的强度稳定性。试验表明, 即使在高于通常的搪烧温度下也能保证钢板具有较高的强度。图1是宝钢BT C330R 经高温搪烧后的力学性能, 可以看出即使经高温长时间的模拟搪烧后钢板的强度下降仍然很小, 也即钢板具有良好的高温稳定性
。
抗鳞爆性能是搪瓷钢板应有的最基本、也是最重要的性能指标之一。导致搪瓷制品产生鳞爆是由氢造成的, 氢主要是在酸洗和搪烧过程中进入钢板的, 所以除了改进搪瓷工艺外, 还应改善钢板本身的抗鳞爆性能。如果氢在钢板中扩散得慢, 在相同的搪瓷工艺下进入钢板中的氢就少, 这将有利于防止搪瓷制品的鳞爆。
钢中的晶界、位错、空穴、夹杂物和析出相等都是良好的氢陷阱, 但超低碳钢由于钢质纯净没有足够的氢陷阱, 满足不了搪瓷时抗鳞爆的需要, 因此对于搪瓷钢, 需要针对不同的搪瓷用途, 调整钢的成分和生产工艺, 以保证钢中有足够的氢陷阱, 实现良好的抗鳞爆性能。
在宝钢生产的搪瓷钢板中, 由于添加了足够的T i 、RE 和B 等合金元素, 它们在钢中与C 、N 和S 元素化合, 形成了足够的第二相粒子, 这些第二相粒子尺寸细小呈弥散分布, 成为良好的贮氢陷阱, 从而提高了钢板的抗鳞爆性能
[3～5]
图1 不同搪烧温度下保温时间对钢板 力学性能的影响4 搪瓷钢的实物性能和应用
典型的宝钢生产的搪瓷钢的实物性能见表4。
。
50
上 海 金 属
表4 搪瓷钢板典型的力学性能
第27卷
牌号
BTC1BTC245R BTC330R
MPa σMPa 厚度Πmm σs Πb Π115210116
140270345
306386454
δ50Π%
504130
n m 0124--
r m 210--
宝钢冷轧搪瓷钢板BT C1和热轧高强度搪瓷钢板BT C330R 的部分应用实例分别见图2和图3。经过大批量的使用证明, 其综合性能完全满
足用户的要求。另外, BT C245R 和BT CR3也具备大批量的供货条件
。
注:表中n m 、r m 值分别为钢板沿与轧制方向呈0°、45°、
90°方向的n 值和r 值的平均值。
(a ) 裙边浴缸 (b ) 建筑饰面板 (c ) 烧烤炉
图2 宝钢BT C1
的应用举例
品, 也可用于替代部分冷轧搪瓷钢板。
宝钢正利用现有的工艺装备继续搪瓷钢板的开发, 以满足用户的不同需求, 为用户的发展提供更大的空间。
参考文献
[1]孙全社等1加钛超低碳钢的成形性能和贮氢性能的研究1
钢铁. 2000, 35(1) :39～42
[2]孙全社等. RE 、T i 和Nb 对冷轧超低碳搪瓷钢板成形性能的
图3 宝钢BT C330R 的应用举例
5 结 语
影响. 钢铁研究学报. (待发表)
[3]孙全社. 冷轧超低碳搪瓷钢板的试验研究. 宝钢技术.
2000, (3) :22～24, 58
[4]袁晓敏, 张庆安, 孙全社. 搪瓷钢板中析出物的测定. 钢
经过几年的开发和实践, 宝钢的搪瓷钢板已基本形成系列化, 能够满足不同用户的需求:
(1) 超深冲冷轧搪瓷钢板具有优良的成形性能(即高的延伸率、高n 值和高r 值) 、无时效性和优良的涂搪性能, 用于深冲浴缸、烧烤炉和建筑饰面板等。
(2) 高强度热轧钢系列不仅具有高强度、良好的成形性、焊接性和涂搪性, 而且经搪烧后具有较高的强度, 能够满足不同冲压难度的热水器内胆的生产要求。
(3) 热轧深冲用钢既具有深冲性能, 又能满足双面搪瓷的要求, 特别适合于生产烧烤炉等产
铁研究学报. 2000, 12(5) :58～60
[5]Sun Quanshe , Jing Lei , Lv Feng , et al. S tudy on Hydrogen
Permeability of T itanium -Bearing Ultra Low Carbon Sheet S teel. Prodeedings of the 4th International HS LA S teels ’2000(in X i ’an ) , edited by Liu G uoquan , W ang Fum ing , W ang Zubin , Zhang H ongtao , organized by the Chinese S ociety for M etals , 635～638[6]安田显ら. 连铸制深绞りほうろう用钢板の制造. 川崎制铁
技报. 1984, 16(4) :280～287; 1994, 34, (1) :17～23
[7]L. M eyer , W. Bleck , W. Muschenborn. Product -oriented IF
S teel Design. ISI J Int. , S pecial Issue on Physical M etallurgy of Ultralow Carbon Interstitial -free S teels. 1994, :203～222
收修改稿日期:2005204220