铜铝异种金属钎焊接头的电化学腐蚀性能研究
【摘 要】通过电化学Tafel 曲线的测试,在室温3.5%氯化钠溶液中,对铜铝异种金属钎焊接头的电化学腐蚀性能进行了研究。结果表明:在钎焊过程中,施加一定压力,在一定的保温温度下,延长保温时间,可以提高接头的耐腐蚀性能。
【关键词】异种金属;焊接接头;腐蚀;电化学
The Research on Corrosion of Dissimilar Metal Connections of Copper and Alloy
ZHU Xiao-ou WANG Xiao-li LU Peng-cheng LUO Chang
(School of Materials Science and Engineering,Jiangsu University of Science and Technology,
Zhenjiang Jiangsu,212003,China )
【Abstract 】The electrochemical corrosion properties of welded joints of Dissimilar Metal Connections of Copper and Alloy were studied by measuring Tafel polarization curves. The results shows that the corrosion resistance of welded joint is better if imposed appropriate pressure and if made it in the longer holding time under the certain temperature.
【Key words】Dissimilar metal;Welded joint;Electrochemical corrosion
随着异种金属连接技术的发展,铝铜钎焊接头由于具有优良的力学性能和导电性能,被广泛地用于电气工程,制冷和供暖设备,以及其他需要铝铜连接的各个领域。目前国内外关于铜铝钎焊报道比较多[1-6],但主要集中于工艺的研究,对其焊缝的电化学腐蚀行为研究的鲜有报道。特别是铜铝接头在焊合后, 由于它的电阻极为微小,随着接头长时间使用或搁之较长时间不运转, 难免会出现腐蚀现象, 从而严重影响了工程构件的安全性。另外由于接头的寿命无法估计, 工艺因素影响复杂, 接头的腐蚀问题已引起广泛的腐蚀科研机构的重视。因此,本文针对四种不同的焊接工艺制备的铜铝钎焊接头进行了电化学实验, 对其接头部位的耐腐蚀性能进行了研究,具有一定的理论意义和工程价值。
1 试验材料及方法
铜铝异种金属钎焊接头的电化学腐蚀性能研究
【摘 要】通过电化学Tafel 曲线的测试,在室温3.5%氯化钠溶液中,对铜铝异种金属钎焊接头的电化学腐蚀性能进行了研究。结果表明:在钎焊过程中,施加一定压力,在一定的保温温度下,延长保温时间,可以提高接头的耐腐蚀性能。
【关键词】异种金属;焊接接头;腐蚀;电化学
The Research on Corrosion of Dissimilar Metal Connections of Copper and Alloy
ZHU Xiao-ou WANG Xiao-li LU Peng-cheng LUO Chang
(School of Materials Science and Engineering,Jiangsu University of Science and Technology,
Zhenjiang Jiangsu,212003,China )
【Abstract 】The electrochemical corrosion properties of welded joints of Dissimilar Metal Connections of Copper and Alloy were studied by measuring Tafel polarization curves. The results shows that the corrosion resistance of welded joint is better if imposed appropriate pressure and if made it in the longer holding time under the certain temperature.
【Key words】Dissimilar metal;Welded joint;Electrochemical corrosion
随着异种金属连接技术的发展,铝铜钎焊接头由于具有优良的力学性能和导电性能,被广泛地用于电气工程,制冷和供暖设备,以及其他需要铝铜连接的各个领域。目前国内外关于铜铝钎焊报道比较多[1-6],但主要集中于工艺的研究,对其焊缝的电化学腐蚀行为研究的鲜有报道。特别是铜铝接头在焊合后, 由于它的电阻极为微小,随着接头长时间使用或搁之较长时间不运转, 难免会出现腐蚀现象, 从而严重影响了工程构件的安全性。另外由于接头的寿命无法估计, 工艺因素影响复杂, 接头的腐蚀问题已引起广泛的腐蚀科研机构的重视。因此,本文针对四种不同的焊接工艺制备的铜铝钎焊接头进行了电化学实验, 对其接头部位的耐腐蚀性能进行了研究,具有一定的理论意义和工程价值。
1 试验材料及方法