废铬酸液综合利用的研究
郭 飞
（安康学院化学化工系，陕西安康，725000）
摘要：利用薯蓣皂素制取双烯醇酮醋酸酯的生产过程中，产生废铬酸液，其中含有大
量的醋酸，同时既有铬（Ⅲ），又有铬（Ⅵ），其中铬（Ⅵ）具有毒性，能引起人体皮肤癌、咽喉癌、肺癌等疾病。废铬酸液的排放不但使宝贵的可利用资源流失，而且还对环境有着较大的危害，所以开展了对废铬酸液综合利用的研究，利用废铬酸液生产两个副产品------醋酸钠和碱式硫酸铬，不仅解决了含铬废酸液排放的环境危害问题，而且达到综合利用的目的。
关键词：废铬酸液 综合利用 醋酸钠 碱式硫酸铬
Diene waste recovery and utilization of chromic acid solution
Abstract: Dioscorea saponin in system take acetic acid double Ene alcohol ketone acetate
ester of production process in the, produced high concentration of with chrome of double Ene waste chrome acid liquid, which contains large of acetic acid and chrome slag, can recycling using resources, waste chrome acid liquid of emissions not only is valuable of can using resources loss, and also on environment has quite of against, so industrial production used has utilization technology, on waste chrome acid liquid for processing, main is on its two a by-products of recycling and using, acetate sodium and chrome slag of of recycling using, reached zero wastewater emissions of production purpose.
目前，我国是最大的甾体激素原料生产国和出口国。在半合成甾体激素的过程中，国内大多生产厂家通常以黄姜（盾叶薯蓣）为植物原料提取薯蓣皂素，再利用薯蓣皂素合成双烯醇酮醋酸酯，继而以双烯醇酮醋酸酯为原料合成各种甾体激素。
利用薯蓣皂素合成双烯醇酮醋酸酯的过程中，一般以薯蓣皂素为原料，经开环裂解反应得到中间产物假薯蓣皂素二醋酸酯，以铬酐作为氧化剂，氧化得产物二酮化合物，继而回流水解生成产物双烯醇酮醋酸酯。该工艺容易产生含铬废酸液，既有铬（Ⅲ），又有铬（Ⅵ），其中铬（Ⅵ）具有毒性，废铬酸液的排放不仅浪费宝贵的可利用资源，而且对环境危害相当大。为了综合利用废铬酸液中的可利用资源，主要是醋酸和铬，以及减少对环境的危害，开展了对废铬酸液综合利用的研究，利用其中的醋酸生产醋酸钠，利用其中的铬生产碱式硫酸铬，本处理方法是在充分查阅国内外资料，反复实验后取得的。本处理方法实用性较强，符合国家对废物“综合利用，化害为利，变废为宝”的方针和经济可持续发展的战略，且具有显著的环境效益、经济效益和社会效益，具有极为广阔的应用前景。
1、废铬酸液
1.1 双烯废铬酸液的产生
在工业生产双烯醇酮醋酸酯的过程中，产生了含铬的废酸酸液，其生产工艺流程如下图1
图1 双烯的生产工艺
1.2废铬酸液的主要成分
以薯蓣皂素为原料在双烯醇酮醋酸酯的生产过程中，辅料有醋酐、冰醋酸、铬酐、醋酸钠，反应完毕，经水洗后产生废铬酸液，其主要成分为稀醋酸和三价铬、六价铬，以及少量的有机物，经过检测其主要成分见下表：
1.3废铬酸液回收工艺流程
在以薯蓣皂素为原料在双烯醇酮醋酸酯的生产过程中，产生高浓度的含铬废酸液，
其中含有大量乙酸等有机物，还含有三价铬和六价铬，六价铬具有毒性。碱式硫酸铬可以用于鞣制皮革，是生产氢氧化铬的原料。染料工业可以用于生产活性黑染料。印染工业可以用作媒染剂。废铬酸液的排放不仅使醋酸和铬这些可利用资源流失，也对环境有一定危害。合理解决废铬酸液排放问题应引起高度重视，对废铬酸液进行综合利用处理，其处理工艺见下图2
纯碱
图2 废铬酸液的回收工艺
2、试验部分
2.1 废铬酸液蒸馏稀醋酸制备醋酸钠的试验
2.1.1实验装置及原料
实验装置：烧杯、玻棒、平底烧瓶、石棉网、电热板、冷凝管、接收器、磁力搅拌器、药匙、结晶槽、离心机。
原料：废铬酸液、硫酸、纯碱。
2.1.2试验反应原理
将蒸馏得到的15～40%稀醋酸装入烧杯中，加入适量纯碱或烧碱发生中和作用，然后将反应后的溶液蒸浓，醋酸钠即结晶而出，反应式如下：
Na 2CO 3+ 2CH3COOH →2CH 3COONa ·3H 2O + H2O+ CO2↑
2.2.3实验步骤
首先将废铬酸液在120-125℃的条件下进行蒸馏，得到15%～40%的稀醋酸，再向蒸馏后的含铬浓浆中加入40-50%的稀硫酸，继续蒸馏，得到15%～40%的稀醋酸，蒸馏的残余物作制备碱式硫酸铬的原料。将稀醋酸加入烧杯中，开启搅拌，用药匙缓缓加入碳酸钠粉末，发生中和作用，至无明显气泡冒出时，测量PH 值，再将反应后的溶液浓缩，冷却结晶，离心甩干后得到醋酸钠。
2.1.4 最佳制备条件
在经过多次试验比较后，醋酸钠的生成和回收，在不同条件下生成和回收率不同，它主要受加入反应物的物料比、PH 值、结晶温度和浓缩液密度影响。
①在PH 值、结晶温度和和浓缩液密度一定条件下，加入不同比的碳酸钠，所制得的醋酸钠的质量不同，见下表1
表1 不同物料比下的产品质量比较
由上表实验数据分析可得，所加入的醋酸和碳酸钠的物料比不能太大也不能太小，加入的醋酸过多了既浪费还有副反应产生，但是醋酸不足了又使反应不完全，有生成物NaHCO3或未反应完全的Na 2CO 3混在产物中，影响产物的纯度。所以最好将投入的醋酸和碳酸钠的物料比控制在1：1.02～1.05之间为宜。
②在物料比、结晶温度和浓缩液密度一定下，不同PH 值的条件下，醋酸钠晶体的质量，见下表2
表2 不同PH 值下产品质量收率
由上表记录的实验数据分析可得：PH 值增大后，产品醋酸含量增加，为了保证质量，PH 值控制在9～10为宜。
③在PH 值、投入的反应物料比和浓缩液密度一定的条件下，在不同结晶温度下醋酸钠晶体质量的一次收率，见下表3
表3 不同结晶温度下产品收率
由上表实验数据分析可得，结晶温度越低收率越高，在20℃以下，醋酸钠晶体的一次收率变化不大，所以醋酸钠结晶温度控制在20℃左右为宜。
④根据最佳投料比投料、结晶温度和PH 值一定的条件下，控制结晶浓缩液的密度，记录相关实验数据，结果见下表4
表4 不同结晶液密度下产品收率
由上表实验数据分析可得，晶体回收率在密度1.25g/cm3后，醋酸钠晶体的回收率明显增大，所以结晶液密度最好控制在1.25g/cm3以上为宜。
从以上试验可以得出，醋酸和碳酸钠的物料比控制在1：1.02～1.05之间，PH 值控制在9～10，结晶温度控制在20℃左右，结晶液密度最好控制在1.25g/cm3以上为最佳条件。
2.1.5实验注意事项
①称取实验物料和配比时尽量做到准确，以便实验记录。 ②蒸馏稀酸时要防止爆沸。
③加入碳酸钠时前期反应较为剧烈，切不可快速加入，每次少量，等到气泡消失后再缓
缓加入，直至无明显气泡产生。 ④反应稳定结束后测定PH 值。
⑤实验完毕后，清洗实验器材，保持器材洁净，以便下次使用。
2.2 碱式硫酸铬的制备
2.2.1实验装置及原料
实验装置：烧杯、玻棒、布氏漏斗、抽滤瓶、真空泵、石棉网、电热板、磁力搅拌器、药匙、碱式滴定管、结晶槽、离心机。
原料：废铬酸液、蔗糖、硫酸、氢氧化钠。 2.1.2实验反应原理
Cr2O72- + H+ + C12H22O11 ——→ Cr3- + CO2 + H2O Cr3- + NaOH + H2SO4 ——→CrOHSO4
2.2.3实验步骤
首先将废铬酸液蒸馏稀醋酸后的残余物加水稀释，放置一段时间，高沸点的大分子有机物会凝聚成沥青状，过滤，可得到含铬的清液，加热至微沸，分批加入蔗糖，然后再过滤，加入氢氧化钠溶液调节PH 值，浓缩后，冷却结晶，离心甩干后得到碱式硫酸铬。
2.1.4最佳制备条件
经过多次实验对比之后，得出所加入蔗糖和Cr(Ⅵ) 的物料比和溶液的PH 值对实验结果有着显著影响。因为Cr(Ⅵ) 除了有毒性外还具有强氧化性，可以使淀粉碘化钾变色，所
由上表实验数据分析可得，蔗糖与总铬含量比为0.25之后时，淀粉碘化钾试纸不再变蓝，而在物料比在0.25之前淀粉碘化钾试纸变蓝色，由其可得，蔗糖与总铬含量的物料比为0.25时最适合反应。
②在制取碱式硫酸铬时，加入NAOH 的量不同，产物的产率不同，在其他条件一定的情况下，控制调节PH 值，在不同PH 值时，记录碱式硫酸铬的回收率，其结果见下表6
由上表实验数据分析可得，PH 值对产品的收率影响很大，PH 值过大或者过小都不适合产品收率，将PH 值控制在6.5～7.5为宜。 2.1.5实验注意事项
①称取实验物料和配比时尽量做到准确，以便实验记录。 ② 加入硫酸蒸馏稀酸时要防止爆沸。
③ 特别注意, 蔗糖还原为放热过程, 反应时会逸出大量的CO 2: 气体和水蒸气, 因此必须控制加糖速度, 防止反应过于剧烈, 突然产生大量气体而造成料液暴沸外溢。 ④ 为使Cr （Ⅵ ）还原完全, 反应终点时须在沸腾状态下进行。 ⑤ 反应稳定结束后测定PH 值。
⑥碱式硫酸铬能引起严重烧伤，有严重损害眼睛的危险，制成碱式硫酸铬回收时注意安全。
⑦实验完毕后，清洗实验器材，保持器材洁净，以便下次使用。
3、结论
在废铬酸液的处理过程中，不同的生产工艺条件，对产品的产率影响不同，在提取醋酸制取醋酸钠晶体和制备碱式硫酸铬时，选择最佳工艺，不仅能最小的投入反应原料，却能最大限度的提高产品回收率。如提取醋酸时，将加入醋酸和碳酸钠的物料比控制在1：1.02～1.05之间，PH 值控制在9～10，结晶温度控制在20℃左右，结晶液密度控制在1.25g/cm3，醋酸钠晶体回收率能达95%以上；制取碱式硫酸铬时加入蔗糖的量与总铬含量的物料比为0.25:1。PH 值控制在6.5～7.5为宜。
4、结束语
在双烯生产过程中，产生大量的含铬废酸液，含铬废酸液中含有大量的乙酸等有机物，还含有六价铬（含有剧毒）。废铬酸液的排放不仅使其中的乙酸浪费，同时也危害环境。所以对双烯生产工艺进行改进，采用综合利用工艺，双烯综合利用生产工艺不仅回收了其中的大量的乙酸，还对铬渣进行了回收利用。从社会效益出发双烯项目社会效益十分显著，一方面推进了甾体激素行业的技术进步，另一方面推动了地区的黄姜种植，带动山区农民脱贫致富。同时新增就业岗位，解决本地一些就业问题。从经济效益出发，新工艺的成功应用，是成本大幅下降，新工艺比老工艺每吨成本下降了3.838万元。每年年产按150吨双烯计算，可年增经济效益575.7万元。从环境效益出发，废铬酸液中的六价铬含有很大的毒性，废铬酸液的排放不仅对环境还对人的健康有相当的危害，双烯废铬酸液的回收利用实现了清洁生产的工业生产目的，废铬酸液重新回收利用生产俩个副产品醋酸钠和铬渣，废水零
排放，在发展经济的同时为确保南水北调工程做出了应有的贡献，具有良好的生态环境效益。
主要参考文献：
[1]王炼翃．利用醋酸废水生产醋酸钠工艺的研究与应用［J ］. 广西轻工业，2007,2,(2):22-24.
[2]钟层玲. 双乙烯酮生产中醋酸回收工艺流程优化[J].天然气化工，2002，27（1）:26-28.
[3]黎小五, 郭正. 双烯醇酮醋酸酯废渣的回收利用[J].湖南化工，2000，30（2）：34-42.
[4]罗华军. 妊娠双烯醇酮醋酸酯的合成工艺研究[J].化学时刊，2006，20（11）：28-45.
[5]马书文. 铬渣治理与资源化综述[J],无机盐工业，1997,(2):19-22. [6]胡术刚, 牛海丽, 张悦忍. 含铬废渣的综合利用研究[J].无机盐工业，2009，41（4）：49-51.
[7]黎小华. 含铬废渣的综合利用[J].重庆环境科学,1995,17(2):47-51. [8]张博, 吴桐, 秦涛, 刘军海. 含铬废水的处理热点及其绿色化发展趋势[J].西部皮革，2009, （17）：36-41.
[9] 孟凡伟，朱元洪，肖勇. 铬渣烧结炼铁的应用研究[J].环境科学与管理，2010，35（11）：116-143.
废铬酸液综合利用的研究
郭 飞
（安康学院化学化工系，陕西安康，725000）
摘要：利用薯蓣皂素制取双烯醇酮醋酸酯的生产过程中，产生废铬酸液，其中含有大
量的醋酸，同时既有铬（Ⅲ），又有铬（Ⅵ），其中铬（Ⅵ）具有毒性，能引起人体皮肤癌、咽喉癌、肺癌等疾病。废铬酸液的排放不但使宝贵的可利用资源流失，而且还对环境有着较大的危害，所以开展了对废铬酸液综合利用的研究，利用废铬酸液生产两个副产品------醋酸钠和碱式硫酸铬，不仅解决了含铬废酸液排放的环境危害问题，而且达到综合利用的目的。
关键词：废铬酸液 综合利用 醋酸钠 碱式硫酸铬
Diene waste recovery and utilization of chromic acid solution
Abstract: Dioscorea saponin in system take acetic acid double Ene alcohol ketone acetate
ester of production process in the, produced high concentration of with chrome of double Ene waste chrome acid liquid, which contains large of acetic acid and chrome slag, can recycling using resources, waste chrome acid liquid of emissions not only is valuable of can using resources loss, and also on environment has quite of against, so industrial production used has utilization technology, on waste chrome acid liquid for processing, main is on its two a by-products of recycling and using, acetate sodium and chrome slag of of recycling using, reached zero wastewater emissions of production purpose.
目前，我国是最大的甾体激素原料生产国和出口国。在半合成甾体激素的过程中，国内大多生产厂家通常以黄姜（盾叶薯蓣）为植物原料提取薯蓣皂素，再利用薯蓣皂素合成双烯醇酮醋酸酯，继而以双烯醇酮醋酸酯为原料合成各种甾体激素。
利用薯蓣皂素合成双烯醇酮醋酸酯的过程中，一般以薯蓣皂素为原料，经开环裂解反应得到中间产物假薯蓣皂素二醋酸酯，以铬酐作为氧化剂，氧化得产物二酮化合物，继而回流水解生成产物双烯醇酮醋酸酯。该工艺容易产生含铬废酸液，既有铬（Ⅲ），又有铬（Ⅵ），其中铬（Ⅵ）具有毒性，废铬酸液的排放不仅浪费宝贵的可利用资源，而且对环境危害相当大。为了综合利用废铬酸液中的可利用资源，主要是醋酸和铬，以及减少对环境的危害，开展了对废铬酸液综合利用的研究，利用其中的醋酸生产醋酸钠，利用其中的铬生产碱式硫酸铬，本处理方法是在充分查阅国内外资料，反复实验后取得的。本处理方法实用性较强，符合国家对废物“综合利用，化害为利，变废为宝”的方针和经济可持续发展的战略，且具有显著的环境效益、经济效益和社会效益，具有极为广阔的应用前景。
1、废铬酸液
1.1 双烯废铬酸液的产生
在工业生产双烯醇酮醋酸酯的过程中，产生了含铬的废酸酸液，其生产工艺流程如下图1
图1 双烯的生产工艺
1.2废铬酸液的主要成分
以薯蓣皂素为原料在双烯醇酮醋酸酯的生产过程中，辅料有醋酐、冰醋酸、铬酐、醋酸钠，反应完毕，经水洗后产生废铬酸液，其主要成分为稀醋酸和三价铬、六价铬，以及少量的有机物，经过检测其主要成分见下表：
1.3废铬酸液回收工艺流程
在以薯蓣皂素为原料在双烯醇酮醋酸酯的生产过程中，产生高浓度的含铬废酸液，
其中含有大量乙酸等有机物，还含有三价铬和六价铬，六价铬具有毒性。碱式硫酸铬可以用于鞣制皮革，是生产氢氧化铬的原料。染料工业可以用于生产活性黑染料。印染工业可以用作媒染剂。废铬酸液的排放不仅使醋酸和铬这些可利用资源流失，也对环境有一定危害。合理解决废铬酸液排放问题应引起高度重视，对废铬酸液进行综合利用处理，其处理工艺见下图2
纯碱
图2 废铬酸液的回收工艺
2、试验部分
2.1 废铬酸液蒸馏稀醋酸制备醋酸钠的试验
2.1.1实验装置及原料
实验装置：烧杯、玻棒、平底烧瓶、石棉网、电热板、冷凝管、接收器、磁力搅拌器、药匙、结晶槽、离心机。
原料：废铬酸液、硫酸、纯碱。
2.1.2试验反应原理
将蒸馏得到的15～40%稀醋酸装入烧杯中，加入适量纯碱或烧碱发生中和作用，然后将反应后的溶液蒸浓，醋酸钠即结晶而出，反应式如下：
Na 2CO 3+ 2CH3COOH →2CH 3COONa ·3H 2O + H2O+ CO2↑
2.2.3实验步骤
首先将废铬酸液在120-125℃的条件下进行蒸馏，得到15%～40%的稀醋酸，再向蒸馏后的含铬浓浆中加入40-50%的稀硫酸，继续蒸馏，得到15%～40%的稀醋酸，蒸馏的残余物作制备碱式硫酸铬的原料。将稀醋酸加入烧杯中，开启搅拌，用药匙缓缓加入碳酸钠粉末，发生中和作用，至无明显气泡冒出时，测量PH 值，再将反应后的溶液浓缩，冷却结晶，离心甩干后得到醋酸钠。
2.1.4 最佳制备条件
在经过多次试验比较后，醋酸钠的生成和回收，在不同条件下生成和回收率不同，它主要受加入反应物的物料比、PH 值、结晶温度和浓缩液密度影响。
①在PH 值、结晶温度和和浓缩液密度一定条件下，加入不同比的碳酸钠，所制得的醋酸钠的质量不同，见下表1
表1 不同物料比下的产品质量比较
由上表实验数据分析可得，所加入的醋酸和碳酸钠的物料比不能太大也不能太小，加入的醋酸过多了既浪费还有副反应产生，但是醋酸不足了又使反应不完全，有生成物NaHCO3或未反应完全的Na 2CO 3混在产物中，影响产物的纯度。所以最好将投入的醋酸和碳酸钠的物料比控制在1：1.02～1.05之间为宜。
②在物料比、结晶温度和浓缩液密度一定下，不同PH 值的条件下，醋酸钠晶体的质量，见下表2
表2 不同PH 值下产品质量收率
由上表记录的实验数据分析可得：PH 值增大后，产品醋酸含量增加，为了保证质量，PH 值控制在9～10为宜。
③在PH 值、投入的反应物料比和浓缩液密度一定的条件下，在不同结晶温度下醋酸钠晶体质量的一次收率，见下表3
表3 不同结晶温度下产品收率
由上表实验数据分析可得，结晶温度越低收率越高，在20℃以下，醋酸钠晶体的一次收率变化不大，所以醋酸钠结晶温度控制在20℃左右为宜。
④根据最佳投料比投料、结晶温度和PH 值一定的条件下，控制结晶浓缩液的密度，记录相关实验数据，结果见下表4
表4 不同结晶液密度下产品收率
由上表实验数据分析可得，晶体回收率在密度1.25g/cm3后，醋酸钠晶体的回收率明显增大，所以结晶液密度最好控制在1.25g/cm3以上为宜。
从以上试验可以得出，醋酸和碳酸钠的物料比控制在1：1.02～1.05之间，PH 值控制在9～10，结晶温度控制在20℃左右，结晶液密度最好控制在1.25g/cm3以上为最佳条件。
2.1.5实验注意事项
①称取实验物料和配比时尽量做到准确，以便实验记录。 ②蒸馏稀酸时要防止爆沸。
③加入碳酸钠时前期反应较为剧烈，切不可快速加入，每次少量，等到气泡消失后再缓
缓加入，直至无明显气泡产生。 ④反应稳定结束后测定PH 值。
⑤实验完毕后，清洗实验器材，保持器材洁净，以便下次使用。
2.2 碱式硫酸铬的制备
2.2.1实验装置及原料
实验装置：烧杯、玻棒、布氏漏斗、抽滤瓶、真空泵、石棉网、电热板、磁力搅拌器、药匙、碱式滴定管、结晶槽、离心机。
原料：废铬酸液、蔗糖、硫酸、氢氧化钠。 2.1.2实验反应原理
Cr2O72- + H+ + C12H22O11 ——→ Cr3- + CO2 + H2O Cr3- + NaOH + H2SO4 ——→CrOHSO4
2.2.3实验步骤
首先将废铬酸液蒸馏稀醋酸后的残余物加水稀释，放置一段时间，高沸点的大分子有机物会凝聚成沥青状，过滤，可得到含铬的清液，加热至微沸，分批加入蔗糖，然后再过滤，加入氢氧化钠溶液调节PH 值，浓缩后，冷却结晶，离心甩干后得到碱式硫酸铬。
2.1.4最佳制备条件
经过多次实验对比之后，得出所加入蔗糖和Cr(Ⅵ) 的物料比和溶液的PH 值对实验结果有着显著影响。因为Cr(Ⅵ) 除了有毒性外还具有强氧化性，可以使淀粉碘化钾变色，所
由上表实验数据分析可得，蔗糖与总铬含量比为0.25之后时，淀粉碘化钾试纸不再变蓝，而在物料比在0.25之前淀粉碘化钾试纸变蓝色，由其可得，蔗糖与总铬含量的物料比为0.25时最适合反应。
②在制取碱式硫酸铬时，加入NAOH 的量不同，产物的产率不同，在其他条件一定的情况下，控制调节PH 值，在不同PH 值时，记录碱式硫酸铬的回收率，其结果见下表6
由上表实验数据分析可得，PH 值对产品的收率影响很大，PH 值过大或者过小都不适合产品收率，将PH 值控制在6.5～7.5为宜。 2.1.5实验注意事项
①称取实验物料和配比时尽量做到准确，以便实验记录。 ② 加入硫酸蒸馏稀酸时要防止爆沸。
③ 特别注意, 蔗糖还原为放热过程, 反应时会逸出大量的CO 2: 气体和水蒸气, 因此必须控制加糖速度, 防止反应过于剧烈, 突然产生大量气体而造成料液暴沸外溢。 ④ 为使Cr （Ⅵ ）还原完全, 反应终点时须在沸腾状态下进行。 ⑤ 反应稳定结束后测定PH 值。
⑥碱式硫酸铬能引起严重烧伤，有严重损害眼睛的危险，制成碱式硫酸铬回收时注意安全。
⑦实验完毕后，清洗实验器材，保持器材洁净，以便下次使用。
3、结论
在废铬酸液的处理过程中，不同的生产工艺条件，对产品的产率影响不同，在提取醋酸制取醋酸钠晶体和制备碱式硫酸铬时，选择最佳工艺，不仅能最小的投入反应原料，却能最大限度的提高产品回收率。如提取醋酸时，将加入醋酸和碳酸钠的物料比控制在1：1.02～1.05之间，PH 值控制在9～10，结晶温度控制在20℃左右，结晶液密度控制在1.25g/cm3，醋酸钠晶体回收率能达95%以上；制取碱式硫酸铬时加入蔗糖的量与总铬含量的物料比为0.25:1。PH 值控制在6.5～7.5为宜。
4、结束语
在双烯生产过程中，产生大量的含铬废酸液，含铬废酸液中含有大量的乙酸等有机物，还含有六价铬（含有剧毒）。废铬酸液的排放不仅使其中的乙酸浪费，同时也危害环境。所以对双烯生产工艺进行改进，采用综合利用工艺，双烯综合利用生产工艺不仅回收了其中的大量的乙酸，还对铬渣进行了回收利用。从社会效益出发双烯项目社会效益十分显著，一方面推进了甾体激素行业的技术进步，另一方面推动了地区的黄姜种植，带动山区农民脱贫致富。同时新增就业岗位，解决本地一些就业问题。从经济效益出发，新工艺的成功应用，是成本大幅下降，新工艺比老工艺每吨成本下降了3.838万元。每年年产按150吨双烯计算，可年增经济效益575.7万元。从环境效益出发，废铬酸液中的六价铬含有很大的毒性，废铬酸液的排放不仅对环境还对人的健康有相当的危害，双烯废铬酸液的回收利用实现了清洁生产的工业生产目的，废铬酸液重新回收利用生产俩个副产品醋酸钠和铬渣，废水零
排放，在发展经济的同时为确保南水北调工程做出了应有的贡献，具有良好的生态环境效益。
主要参考文献：
[1]王炼翃．利用醋酸废水生产醋酸钠工艺的研究与应用［J ］. 广西轻工业，2007,2,(2):22-24.
[2]钟层玲. 双乙烯酮生产中醋酸回收工艺流程优化[J].天然气化工，2002，27（1）:26-28.
[3]黎小五, 郭正. 双烯醇酮醋酸酯废渣的回收利用[J].湖南化工，2000，30（2）：34-42.
[4]罗华军. 妊娠双烯醇酮醋酸酯的合成工艺研究[J].化学时刊，2006，20（11）：28-45.
[5]马书文. 铬渣治理与资源化综述[J],无机盐工业，1997,(2):19-22. [6]胡术刚, 牛海丽, 张悦忍. 含铬废渣的综合利用研究[J].无机盐工业，2009，41（4）：49-51.
[7]黎小华. 含铬废渣的综合利用[J].重庆环境科学,1995,17(2):47-51. [8]张博, 吴桐, 秦涛, 刘军海. 含铬废水的处理热点及其绿色化发展趋势[J].西部皮革，2009, （17）：36-41.
[9] 孟凡伟，朱元洪，肖勇. 铬渣烧结炼铁的应用研究[J].环境科学与管理，2010，35（11）：116-143.