蒸压轻质砂加气混凝土(AAC)砌块的应用
李健 中国石油大学（华东）规划建设处
Application In Engineering of Autoclaved Aerated Concrete Block ( AAC)
Li Jian
（Planning and Construction Department, China University of Petroleum,266555,Qingdao,
China ）
摘要 中国石油大学（华东）留学生及培训生综合楼外墙应用了一种节能墙体材料——蒸压轻质砂加气混凝土砌块(AAC) ，是目前国内大力推广的一种墙体材料。相比于传统的砌筑产品，AAC 具有质轻、保温、隔热、防火等优良特性，而且可加工性能好、施工速度快。AAC 采用薄层砌筑工艺灰缝小（2-3mm ），有效减少墙体复合应力，从而增加墙体有效强度，使抗震性能大为提高。同时，作为一种新型的自保温材料，不但能够满足墙材革新的要求，同时也能满足严格的节能要求。
关键词 AAC 外墙保温 节能
Abstract : China university of petroleum (east China) students and trainees application of the outside wall of a kind of energy-saving wall materials - sand autoclaved lightweight aerated concrete lock (AAC), is the present domestic promoted a kind of wall materials. Compared to the raditional masonry products, AAC is qualitative light, heat preservation, heat insulation, excellent features, such as fire prevention and processing performance is good, fast construction speed. AAC laying process was used to ash seam small (2-3 mm), effectively reduce wall complex stress, thus increasing the wall effective strength, has greatly improve seismic performance. At the same time, as a kind of new type thermal insulation material, not only can satisfy the requirements of the wall materials innovation, at the same time also can meet strict energy saving requirements. Abstract AAC ; exterior wall thermal insulation; energy saving 1、 工程概况
中国石油大学（华东）青岛校区留学生及培训生综合楼建筑面积约45000㎡，结构形式为框架剪力墙结构，建筑高度约52米，拟建场区位于青岛经济技术开发区，南侧为唐岛湾，夏季较湿热，冬季寒冷。因濒临开发区主要景观大道，外墙需要石材装饰。 2、 墙体材料的选择
目前建筑中应用的墙体材料有普通加气混凝土砌块、烧结页岩大孔砖及近几年大力推广的新型蒸压轻质砂加气混凝土砌块。烧结页岩大孔砖导热系数约为0.81W/( m.K) ，普通加气混凝土砌块为0.23 W/( m.K)，新型蒸压轻质砂加气混凝土砌块导热系数能够达到为0.13 W/( m.K)。根据本工程特点，若选用烧结页岩大孔砖，热工计算如下表：
表1 热工计算表
Table 1 The thermal calculation table
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）
若选用蒸压轻质砂加气混凝土砌块，热工计算如下表：
表2 热工计算表
Table 1 The thermal calculation table
通过以上热工计算，如果采用烧结页岩大孔砖（或普通加气混凝土砌块）则需外贴岩棉或其他保温材料才能满足节能要求，会增加施工难度及工期；而采用新型蒸压轻质砂加气混凝土砌块，外墙达到250厚时，不粘贴其他保温材料，即可满足节能需求。
比较两种方案的综合造价，见下表：
表3 综合造价比较
Table 3 Comprehensive cost comparison
从上表可以得出，采用AAC 砌筑造价更低，因此本工程选用AAC 砌筑。 3、 施工方法
1）确定本工程外围护墙采用600mmx250mmx250mm 尺寸，内隔墙选用600mmx250mmx200mm 尺寸。在楼层砌筑砌体的位置弹出墙体边线、门窗洞口等定位线，然后在各转角处设立皮树杆，且皮书杆间距不得大于15m ，皮树杆上注明门窗洞口、配筋带、专用过梁的标高，皮树杆要垂直、标高一致。第一皮砌块砌筑前，要先用水润湿基面，再施铺M7.5专用水泥砂浆，并在砌块底面水平灰缝和侧面垂直灰缝满涂粘结剂后进行砌筑。第二皮砌块的砌筑，必须待第一皮砌块水平灰缝的砌筑砂浆初凝后方能进行，灰缝厚度为2-3mm ，砌筑要错缝搭接，搭接长度不小于100mm 。
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）
图1 墙体与框架拉结水平布置示意图
Figure 1 Rachel wall and frame horizontal layout diagram
2）当墙体长度超过层高2倍或长度大于6m 时设置构造柱。本工程采用方钢管构造柱。 4、蒸压轻质砂加气混凝土砌块应用优点
1．重量轻。本工程采用的B5型蒸压轻质砂加气混凝土砌块密度为505kg/m3，比大孔页岩砖轻300kg 左右，可大大降低基础和结构处理的费用。
2．定尺精确，施工方便。AAC 砌块强度较高，可任意切割；定尺精确，安装轻便，减少抹灰工序，并且构造柱可采用钢柱，省略掉混凝土构造柱的钢筋绑扎和混凝土浇筑程序；由于可加工性好，并且一块常规砌块相当于近20块页岩砖体积，砌筑速度较快而且不受一次砌筑高度限制，可有效缩短工期。
3. 耐火、隔音、抗渗性能好。AAC 在700℃高温下很长时间内不会损失强度，亦不产生有毒气体。20公分厚的墙体防火能力可达8小时以上，耐火极限可满足建筑设计防火规范对防火墙的防火要求，是理想的一级防火建筑材料。 该产品内部小孔均为独立封闭孔，直径约为1-2mm ，能有效地阻止水分扩散。采用专用粘结剂砌筑更进一步提高了墙面整体的防渗性。同时因为封闭小孔，计权隔声量可达40-50Db ，也是一种良好的吸音材料。
4. 经济效益好。保温性能良好使其可以作为自保温外墙，省去外墙另做保温费用，施工工期缩短亦可降低施工成本。 5、结论
中国石油大学（华东）留学生及培训生综合楼采用的蒸压轻质砂加气混凝土砌块效果良好。使用AAC 后降低了工程造价，大大节省了工程工期，且在施工过程中基本不使用水泥砂浆，环境保持良好，做到了文明施工。AAC 是青岛市政府着力推广的新型保温砌体材料，在该工程的成功应用预示着该项材料必将得到更为广阔的发展空间。 参考文献
[ 1 ]朱国梁, 周小强, 张国峰. 蒸压加气砼砌块的应用[J ] . 建筑知识,1996 (3):7-8. [ 2 ]李恩华. 轻质砂加气混凝土砌块在工程中的使用[J ] . 砖瓦,2005(5):105-106. [ 3 ]沈勤. 《蒸压轻质砂加气混凝土砌块应用技术规程》的应用[J ] . 天津建设科技,2005,15 (6):24.
作者简介
【（第一）作者简介】李健：男，山东梁山县人，1980年生，工程师，2003年毕业于中国石油大学（华东）土木工程专业，主要从事土木工程研究。（0532）86981756、[1**********]、lj@upc.edu.cn。
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）
蒸压轻质砂加气混凝土(AAC)砌块的应用
李健 中国石油大学（华东）规划建设处
Application In Engineering of Autoclaved Aerated Concrete Block ( AAC)
Li Jian
（Planning and Construction Department, China University of Petroleum,266555,Qingdao,
China ）
摘要 中国石油大学（华东）留学生及培训生综合楼外墙应用了一种节能墙体材料——蒸压轻质砂加气混凝土砌块(AAC) ，是目前国内大力推广的一种墙体材料。相比于传统的砌筑产品，AAC 具有质轻、保温、隔热、防火等优良特性，而且可加工性能好、施工速度快。AAC 采用薄层砌筑工艺灰缝小（2-3mm ），有效减少墙体复合应力，从而增加墙体有效强度，使抗震性能大为提高。同时，作为一种新型的自保温材料，不但能够满足墙材革新的要求，同时也能满足严格的节能要求。
关键词 AAC 外墙保温 节能
Abstract : China university of petroleum (east China) students and trainees application of the outside wall of a kind of energy-saving wall materials - sand autoclaved lightweight aerated concrete lock (AAC), is the present domestic promoted a kind of wall materials. Compared to the raditional masonry products, AAC is qualitative light, heat preservation, heat insulation, excellent features, such as fire prevention and processing performance is good, fast construction speed. AAC laying process was used to ash seam small (2-3 mm), effectively reduce wall complex stress, thus increasing the wall effective strength, has greatly improve seismic performance. At the same time, as a kind of new type thermal insulation material, not only can satisfy the requirements of the wall materials innovation, at the same time also can meet strict energy saving requirements. Abstract AAC ; exterior wall thermal insulation; energy saving 1、 工程概况
中国石油大学（华东）青岛校区留学生及培训生综合楼建筑面积约45000㎡，结构形式为框架剪力墙结构，建筑高度约52米，拟建场区位于青岛经济技术开发区，南侧为唐岛湾，夏季较湿热，冬季寒冷。因濒临开发区主要景观大道，外墙需要石材装饰。 2、 墙体材料的选择
目前建筑中应用的墙体材料有普通加气混凝土砌块、烧结页岩大孔砖及近几年大力推广的新型蒸压轻质砂加气混凝土砌块。烧结页岩大孔砖导热系数约为0.81W/( m.K) ，普通加气混凝土砌块为0.23 W/( m.K)，新型蒸压轻质砂加气混凝土砌块导热系数能够达到为0.13 W/( m.K)。根据本工程特点，若选用烧结页岩大孔砖，热工计算如下表：
表1 热工计算表
Table 1 The thermal calculation table
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）
若选用蒸压轻质砂加气混凝土砌块，热工计算如下表：
表2 热工计算表
Table 1 The thermal calculation table
通过以上热工计算，如果采用烧结页岩大孔砖（或普通加气混凝土砌块）则需外贴岩棉或其他保温材料才能满足节能要求，会增加施工难度及工期；而采用新型蒸压轻质砂加气混凝土砌块，外墙达到250厚时，不粘贴其他保温材料，即可满足节能需求。
比较两种方案的综合造价，见下表：
表3 综合造价比较
Table 3 Comprehensive cost comparison
从上表可以得出，采用AAC 砌筑造价更低，因此本工程选用AAC 砌筑。 3、 施工方法
1）确定本工程外围护墙采用600mmx250mmx250mm 尺寸，内隔墙选用600mmx250mmx200mm 尺寸。在楼层砌筑砌体的位置弹出墙体边线、门窗洞口等定位线，然后在各转角处设立皮树杆，且皮书杆间距不得大于15m ，皮树杆上注明门窗洞口、配筋带、专用过梁的标高，皮树杆要垂直、标高一致。第一皮砌块砌筑前，要先用水润湿基面，再施铺M7.5专用水泥砂浆，并在砌块底面水平灰缝和侧面垂直灰缝满涂粘结剂后进行砌筑。第二皮砌块的砌筑，必须待第一皮砌块水平灰缝的砌筑砂浆初凝后方能进行，灰缝厚度为2-3mm ，砌筑要错缝搭接，搭接长度不小于100mm 。
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）
图1 墙体与框架拉结水平布置示意图
Figure 1 Rachel wall and frame horizontal layout diagram
2）当墙体长度超过层高2倍或长度大于6m 时设置构造柱。本工程采用方钢管构造柱。 4、蒸压轻质砂加气混凝土砌块应用优点
1．重量轻。本工程采用的B5型蒸压轻质砂加气混凝土砌块密度为505kg/m3，比大孔页岩砖轻300kg 左右，可大大降低基础和结构处理的费用。
2．定尺精确，施工方便。AAC 砌块强度较高，可任意切割；定尺精确，安装轻便，减少抹灰工序，并且构造柱可采用钢柱，省略掉混凝土构造柱的钢筋绑扎和混凝土浇筑程序；由于可加工性好，并且一块常规砌块相当于近20块页岩砖体积，砌筑速度较快而且不受一次砌筑高度限制，可有效缩短工期。
3. 耐火、隔音、抗渗性能好。AAC 在700℃高温下很长时间内不会损失强度，亦不产生有毒气体。20公分厚的墙体防火能力可达8小时以上，耐火极限可满足建筑设计防火规范对防火墙的防火要求，是理想的一级防火建筑材料。 该产品内部小孔均为独立封闭孔，直径约为1-2mm ，能有效地阻止水分扩散。采用专用粘结剂砌筑更进一步提高了墙面整体的防渗性。同时因为封闭小孔，计权隔声量可达40-50Db ，也是一种良好的吸音材料。
4. 经济效益好。保温性能良好使其可以作为自保温外墙，省去外墙另做保温费用，施工工期缩短亦可降低施工成本。 5、结论
中国石油大学（华东）留学生及培训生综合楼采用的蒸压轻质砂加气混凝土砌块效果良好。使用AAC 后降低了工程造价，大大节省了工程工期，且在施工过程中基本不使用水泥砂浆，环境保持良好，做到了文明施工。AAC 是青岛市政府着力推广的新型保温砌体材料，在该工程的成功应用预示着该项材料必将得到更为广阔的发展空间。 参考文献
[ 1 ]朱国梁, 周小强, 张国峰. 蒸压加气砼砌块的应用[J ] . 建筑知识,1996 (3):7-8. [ 2 ]李恩华. 轻质砂加气混凝土砌块在工程中的使用[J ] . 砖瓦,2005(5):105-106. [ 3 ]沈勤. 《蒸压轻质砂加气混凝土砌块应用技术规程》的应用[J ] . 天津建设科技,2005,15 (6):24.
作者简介
【（第一）作者简介】李健：男，山东梁山县人，1980年生，工程师，2003年毕业于中国石油大学（华东）土木工程专业，主要从事土木工程研究。（0532）86981756、[1**********]、lj@upc.edu.cn。
【基金项目】：青岛市施工现场观摩项目（AAC 砌块是青岛市大力推广用节能材料）